微纳纤维素与聚砜共混体系相容性的研究

生物质化学工程 ›› 2009, Vol. 43 ›› Issue (2): 15-18.

微纳纤维素与聚砜共混体系相容性的研究

唐焕威, 张力平, 林星

北京林业大学, 材料科学与技术学院, 北京, 100083

收稿日期:2008-09-24 修回日期:1900-01-01 出版日期:2009-03-30 发布日期:2009-03-30
通讯作者: 张力平(1959- ),女,北京人,副教授,博士,主要研究方向为功能高分子材料;联系电话:010-62338152.E-mail:zhanglp418@163.com.

The Research of Miscibility of Micro/Nano-crystal Cellulose and Polysulphone Blend System

TANG Huan-wei, ZHANG Li-ping, LIN Xing

College of Material Science and Technology, Beijing Forestry University, Beijing 100083, China

Received:2008-09-24 Revised:1900-01-01 Online:2009-03-30 Published:2009-03-30

摘要/Abstract

摘要： 通过微纳纤维素一聚砜制膜液的水通量、截留率、黏度的测定、相分离结构分析及凝胶特性分析等,研究其共混体系的相容性.研究结果表明,一定共混比例下,微纳纤维素在聚砜制膜液中分散均匀,黏度曲线呈非线性,该共混体系为部分相容体系.当聚砜质量分数18%,添加剂为PVP K30,添加质量分数为0.3%,蒸发时间为10 s,凝胶浴为水的制膜条件下,微纳纤维素质量分数为5.%时,复合超滤膜水通量最高可达235.27 L/(m²·h),截留率达95.35%.随着凝胶浴温度升高,复合超滤膜膜孔的梯度变好.

关键词: 微纳纤维素, 聚砜, 相容性, 超滤膜

Abstract: The miscibility of micro/nano-crystal cellulose/polysulphone blend system was studied by determination of absolute viscosity, and analysis of phase separation structure and coagulation properties of blend system, as well as determination of water flux and rejection ratio of the composite membrane. Under different temperatures of coagulation bath, the structure of membrane was examined by SEM. These results indicated that at a certain proportion scale micro/nano-crystal cellulose were equably dispersed in PSF casting solution. The blend system was semimiscible with a nonlinear viscosity curve. Under the condition of 18% polysulphone, PVP K30 as additive in 0.3% mass fraction, 10 s evaporation time, 5.4% micro/nano-crystal cellulose the pure water flux of the composite membrane could reach 235.27 L/(m²·h) and the rejection ratio was 95.35%.The gradient of membrane poles became better, with the increasing of temperature of coagulation bath.

Key words: micro/nano-crystal cellulose, polysulphone, miscibility, ultrafiltration membrane

中图分类号:

TQ352.79

唐焕威;张力平;林星. 微纳纤维素与聚砜共混体系相容性的研究[J]. 生物质化学工程, 2009, 43(2): 15-18.

TANG Huan-wei;ZHANG Li-ping;LIN Xing. The Research of Miscibility of Micro/Nano-crystal Cellulose and Polysulphone Blend System[J]. , 2009, 43(2): 15-18.

[1]	吴晨曦, 叶哲孜, 乐喜, 王鹏, 谢益民. 杨木MWL和LCC制备多孔生物载体及其在人体肝细胞培养中的应用[J]. 生物质化学工程, 2016, 50(5): 7-11.
[2]	徐浩;张宗和;仲崇茂;秦清;陶林;王光辉. 膜分离法制备塔拉单宁的研究[J]. 生物质化学工程, 2009, 43(1): 17-19.
[3]	张力平;陈国伟;唐焕威;王思群. 聚砜-纤维素复合超滤膜材料的制备与表征[J]. 生物质化学工程, 2008, 42(1): 11-16.