超声波辅助纤维素酶水解制备纳米纤维素

doi:10.3969/j.issn.1673-5854.2020.01.009

Abstract

Abstract:

Nanocellulose(NCC) was prepared with cellulose pulp as raw material by using cellulase hydrolysis under sonication-assisted technology. Orthogonal test was used to optimize the preparation of NCC on the basis of single factor test. The structure and properties of NCC were analyzed and characterized by transmission electron microscope(TEM), X-ray diffraction(XRD), infrared spectroscopy(FT-IR), thermogravimetry(TG) and Zeta potential measurement. The results showed that the yield of 62.3% for NCC could be achieved when the cellulase dosage was 7%, reaction temperature was 50℃ and reaction time was 10 h. TEM image showed that the prepared NCC was short rod-like, which interacted with each other to form a web-like network. XRD results suggested that the crystal structure of NCC was cellulose I, and the crystallinity increased from 54.2% to 73%. FT-IR implied that the original chemical structure of NCC was not altered. TGA analysis indicated that the thermal stability of NCC was significantly improved compared with that of cellulose pulp. The Zeta potential test showed that NCC suspension had good dispersion stability in aqueous medium.

Key words: nanocellulose, cellulase, sonication, green, high-efficient

CLC Number:

TQ352

Linna LU,Qilin LU. Preparation of Nanocellulose by Cellulase Hydrolysis Under Sonication-assisted[J]. Biomass Chemical Engineering, 2020, 54(1): 55-59.

Figures/Tables 7

Fig.1

Table 1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

References 14

1	OKSMAN K , SAIN M . Cellulose Nanocomposites:Processing, Characterization and Properties[M]. Oxford: Oxford University Press Inc, 2006.
2	MANTIA F P L , MORREALE M . Green composites:A brief review[J]. Composites Part A:Applied Science & Manufacturing, 2011, 42 (6): 579- 588.
3	PANDEY J K , AHN S H , LEE C S , et al. Recent advances in the application of natural fiber based composites[J]. Macromolecular Materials & Engineering, 2010, 295 (11): 975- 989.
4	YARBROUGH J M , ZHANG R , MITTAL A , et al. Multifunctional cellulolytic enzymes outperform processive fungal cellulases for coproduction of nanocellulose and biofuels[J]. ACS Nano, 2017, 11 (3): 3101- 3109.
5	WANG H K , ZHANG X X , JIANG Z H , et al. A comparison study on the preparation of nanocellulose fibrils from fibers and parenchymal cells in bamboo(Phyllostachys pubescens)[J]. Industrial Crops and Products, 2015, 71, 80- 88.
6	BEYER M K , CLAUSENSCHAUMANN H . Mechanochemistry:The mechanical activation of covalent bonds[J]. Chemical Reviews, 2005, 105 (8): 2921- 2948.
7	GHANBARI A , TABARSA T , ASHORI A , et al. Preparation and characterization of thermoplastic starch and cellulose nanofibers as green nanocomposites:Extrusion processing[J]. International Journal of Biological Macromolecules, 2018, 112 (6): 442- 447.
8	ZHANG W , LIANG M , LU C H . Morphological and structural development of hardwood cellulose during mechanochemical pretreatment in solid state through pan-milling[J]. Cellulose, 2007, 14 (5): 447- 456.
9	HAYASHI N , KONDO T , ISHIHARA M . Enzymatically produced nano-ordered short elements containing cellulose I_β crystalline domains[J]. Carbohydrate Polymers, 2005, 61 (2): 191- 197.
10	ABRAHAM E , THOMAS M S , JOHN C , et al. Green nanocomposites of natural rubber/nanocellulose:Membrane transport, rheological and thermal degradation characterisations[J]. Industrial Crops & Products, 2013, 51 (6): 415- 424.
11	FRENCH A D . Idealized powder diffraction patterns for cellulose polymorphs[J]. Cellulose, 2014, 21 (2): 885- 896.
12	SEGAL L C , CREELY J , MARTIN A E J , et al. An empirical method for estimating the degree of crystallinity of native cellulose using the X-ray diffractometer[J]. Textile Research Journal, 1959, 29 (10): 786- 794.
13	HAMID S B , ZAIN S K , DAS R , et al. Synergic effect of tungstophosphoric acid and sonication for rapid synthesis of crystalline nanocellulose[J]. Carbohydrate Polymers, 2016, 138 (3): 349- 355.
14	MIRHOSSEINI H , TAN C P , HAMID N S A , et al. Effect of Arabic gum, xanthan gum and orange oil contents on zeta-potential, conductivity, stability, size index and pH of orange beverage emulsion[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2008, 315 (1/2/3): 47- 56.

序号 No.	A 纤维素酶用量/% cellulase dosage	B 酶解温度/℃ enzymolysis temperature	C 酶解时间/h enzymolysis time	得率/% yield
1	7	45	9	38.6
2	7	50	10	62.3
3	7	55	11	27.1
4	8	45	10	42.0
5	8	50	11	51.7
6	8	55	9	28.1
7	6	45	11	24.4
8	6	50	9	41.4
9	6	55	10	29.9
k₁	42.67	35.00	36.03
k₂	40.60	51.80	44.73
k₃	31.90	28.37	34.40
R	10.77	23.43	10.33

[1]	Weijiao SHANG,Lu WANG. Status and Analysis of Nanocellulose Technology Based on Patents [J]. Biomass Chemical Engineering, 2020, 54(4): 49-56.
[2]	Lin SUN,Huayu LIU,Kun LIU,Xiaoyi ZHANG,Hongxiang XIE,Rui ZHANG,Haiming LI,Chuanling SI. Research Progress in Nanocellulose Hydrophobic Modification and Applications [J]. Biomass Chemical Engineering, 2020, 54(4): 57-66.
[3]	Xiangxing SHI,Hongchuan SONG,Ying HUANG,Kemei ZHOU. Current Situation and Countermeasures of Hydroprocessing Biofuels Development in Large Petrochemical Corporation [J]. Biomass Chemical Engineering, 2019, 53(4): 59-66.
[4]	Heng ZHANG,Hongkun GAO,Zhe WANG,Xiaolong ZHU,Dongyang LIU. Progress in Preparation and Application of Hydrophobized Modified Nanocellulose [J]. Biomass Chemical Engineering, 2019, 53(1): 61-66.
[5]	LIU Junli, JIANG Jianchun. Green Development of Forest Product Industry Driven by Innovation [J]. bce, 2018, 52(4): 36-44.
[6]	YANG Xuan, TANG Lirong, LIN Fengcai, LU Qilin, HUANG Biao. Preparation and Properties of Nanocellulose/Chitosan/Gelatin Composite Films [J]. bce, 2018, 52(1): 17-22.
[7]	CHEN Jiajie, LI Xinping, CHEN Shuai, WANG Zhijie, CHEN Lihong. Effect of Enzymatic Pretreatment on Pore Structure of Bleached Wheat Straw Fiber [J]. bce, 2017, 51(1): 27-32.
[8]	JIANG Lu, WANG Bu-cheng, BAI He-chao, YONG Qiang, YU Shi-yuan. Influence of Periodic Enzyme and Mycelia Recovery on Cellulase Production by Trichoderma reesei [J]. bce, 2016, 50(6): 49-55.
[9]	WANG Yan-yun, WU Kai, LEI Fu-hou, YANG Jing. Process Resrarch of Multi-stage Enzymatic Hydrolysis of NaOH-Fenton Pretreated Mulberry Wood [J]. bce, 2016, 50(4): 31-36.
[10]	ZHANG Kai-tao, SUN Pei-pei, SHANG Shi-bin, LIU He, WANG Dan, LI Jing-jing. Preparation of Nanocellulose and Its Aerogel from Bagasse Pulp [J]. bce, 2015, 49(5): 7-10.
[11]	ZHANG Ning, JIANG Jian-chun, YANG Jing, WEI Min, ZHAO Jian, TONG Ya-juan. Study on the Fermentation of Cellulase Solid Koji by Using Trichoderma reesei [J]. bce, 2014, 48(5): 7-10.
[12]	ZHANG Ning, JIANG Jian-chun, YANG Jing, WEI Min, ZHAO Jian, TONG Ya-juan. Screening of High-producing Cellulase Strain by Low Energy N⁺ Implantation and Optimization of Fermentation Nutrient Factors [J]. bce, 2014, 48(4): 28-34.
[13]	WU Qiao-mei, CHEN Yan-dan, HUANG Biao, CHEN Xue-rong. Advances in Inorganic-nanocellulose Hybrid Nanomaterials [J]. bce, 2014, 48(1): 28-36.
[14]	WANG Jian;CHANG Qing;TIAN Bing-hui;YUAN Xian-zheng;PAN Feng. Life Cycle Assessment of Chemical Pollutant Discharge Risk for Biodiesel Made from Rapeseed [J]. , 2013, 47(3): 17-22.
[15]	ZHONG Jian;YUE Yang;SHI Jia-ji;SUN Yan;CHAO Ya-peng;QIAN Shi-jun. Process of Neutral Cellulase-based Saccharification on the Neutral Steam Exploded Corn Stover [J]. , 2013, 47(2): 9-14.

Preparation of Nanocellulose by Cellulase Hydrolysis Under Sonication-assisted

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 7

References 14

Related Articles 15

Recommended Articles

Metrics

Comments