Abstract: Using bamboo cellulose as raw materials, bamboo cellulose-acrylate emulsion pressure-sensitive adhesive was synthetized by semi-continuous emulsion polymerization method. The results showed that: when the polymerization system temperature 85℃, stirring rate 150 r/min, the hard and soft monomer ratio 4:1, hard monomers methacrylic acid:vinyl acetate 1:4, initiator dosage 0.30%, adding 0.6% of the total mass fraction of bamboo cellulose and reaction time of 3h were used, good performance pressure-sensitive adhesive with viscosity of 21.3 mPa·s, the peel strength of 0.692 N/mm could be obtained, The results provide a useful reference for the new bamboo cellulose matrix pressure-sensitive adhesive.

Key words: acrylate, bamboo cellulose, pressure sensitive adhesive, polymerization