The Preliminary Study of Non-drying Oil Polymerization

WANG Hai-qing, LONG Xiao-yan, WANG Zheng-hui   

  1. Department of Applied Chemistry, South China Agricultural University, Guangzhou 510642, China
  • Received:2007-11-21 Revised:1900-01-01 Online:2008-09-30 Published:2008-09-30

Abstract: The polymerization results of non-drying oil including soybean oil and lard with ethyl acrylate and ethylene glycol dimethacrylate as accelerators, as well as benzoyl peroxide and dimethyl aniline as initiators, were prelimilarily reported in this paper. When the mass ratio of soybean oil to lard was 6 to 4, the mass percentages for biomass mixed oil, ethyl acrylate, ethy-lene glycol dimethacrylate were 40%, 55%, 5%, respectively, and the initiator accounted for 1% in total material, a polymer with hard rubber status was obtained at room temperature in 5min. The FT-IR spectra provided the evidence that non-drying oil took part in polymerization. The TG data showed that the polymer with 40% oil had excellent thermal stability below 240℃.

Key words: non-drying oil, polymerization, thermal stability