胶合板用尿素改性酚醛树脂胶合性能的研究

doi:10.3969/j.issn.1673-5854.2018.05.004

生物质化学工程 ›› 2018, Vol. 52 ›› Issue (5): 20-24.doi: 10.3969/j.issn.1673-5854.2018.05.004

胶合板用尿素改性酚醛树脂胶合性能的研究

王荣兴, 张祖新, 陈日清, 赵临五, 王春鹏

中国林业科学研究院林产化学工业研究所;生物质化学利用国家工程实验室;国家林业局林产化学工程重点开放性实验室;江苏省生物质能源与材料重点实验室, 江苏南京 210042

收稿日期:2017-04-28 出版日期:2018-09-30 发布日期:2018-10-15
通讯作者: 陈日清,副研究员,硕士生导师,主要从事生物基高分子研究;E-mail:michaelmao77@163.com。 E-mail:michaelmao77@163.com
作者简介:王荣兴(1993-),男,山东桓台人,硕士,研究方向生物基高分子材料
基金资助:
“十二五”国家科技支撑计划资助（2015BAD14B03）；木竹产业技术创新战略科研计划资助（TIAWBI201506）

Adhesion Properties of Urea-modified Phenol Formaldehyde Resin for Plywood

WANG Rongxing, ZHANG Zuxin, CHEN Riqing, ZHAO Linwu, WANG Chunpeng

Institute of Chemical Industry of Forest Products, CAF;National Engineering Lab. for Biomass Chemical Utilization;Key and Open Lab. of Forest Chemical Engineering, SFA;Key Lab. of Biomass Energy and Material, Jiangsu Province, Nanjing 210042, China

Received:2017-04-28 Online:2018-09-30 Published:2018-10-15

摘要/Abstract

摘要： 制备了不同尿素用量的系列尿素改性酚醛（PUF）树脂体系（当尿素用量为苯酚质量的0、25%、43%、66%时分别记为PF、PUF-1、PUF-2、PUF-3），并将其用于制备胶合板，研究树脂在胶合板加工过程中的变化。结果表明：PUF-3树脂与桉木和杨木的接触角为79.6°和81.1°，小于PF树脂的，PUF对桉木相容性比杨木优良，PF树脂则相反；对4种树脂进行DSC分析显示，PF、PUF-1、PUF-2、PUF-3固化速率最大温度分别为146.8、171.4、171.8和171.8℃；PUF-3和面粉共混体系的流变行为显示该共混体系110℃开始发生固化反应，（130±5）℃为较合适的热压温度；对热压前后PF和PUF-3进行热重分析，结果发现PUF的耐高温性能优于PF，热压后形成的结构耐热性也更好；4种树脂压制的胶合板性能达到E₀级，甲醛释放量均小于0.5mg/L，胶合强度分别为1.42、1.11、0.98和0.92MPa。

关键词: 尿素改性酚醛树脂, 木材胶黏剂, 人造板, 加工工艺

Abstract: A series of urea-modified phenol formaldehyde(PUF) resin systems with different urea contents were prepared and used in the preparation of plywood(when the dosages of urea(U) were 0, 25%, 43% and 66% of the mass of phenol(P), the obtained samples were recorded as PF, PUF-1, PUF-2 and PUF-3). The resins were used for preparing plywood and the change of resins during plywood processing was studied. The results showed that the contact angles of the PUF-3 resin with eucalyptus and poplar were 79.6ånd 81.1°, and the compatibility of PUF to eucalyptus wood was better than that of poplar wood. And the curing processes of four kinds of resins were obtained by DSC analysis. The temperatures of maximum curing rate of PF, PUF-1, PUF-2 and PUF-3 were 146.8, 171.4, 171.8 and 171.8℃. The rheological behavior of the complex system formed by mixing PUF-3 with flour was studied by means of rotating rheometer, and the curing reaction began to occur at 110℃, and the suitable hot-pressing temperature was (130±5)℃. The thermogravimetric analysis of PF and PUF-3 before and after hot pressing showed that the high temperature resistance of PUF was better than that of PF, and the heat resistance of structure formed by hot pressing was better. The properties of plywood produced with the four resins were qualified and reached E₀ level, the formaldehyde emission of eucalyptus plywood was less than 0.5mg/L, and the bonding strengths of plywood were 1.42, 1.11, 0.98 and 0.92MPa, respectively.

Key words: urea-modified phenol formaldehyde resin, wood adhesive, artificial board, processing technology

中图分类号:

TQ35

王荣兴, 张祖新, 陈日清, 赵临五, 王春鹏. 胶合板用尿素改性酚醛树脂胶合性能的研究[J]. 生物质化学工程, 2018, 52(5): 20-24.

WANG Rongxing, ZHANG Zuxin, CHEN Riqing, ZHAO Linwu, WANG Chunpeng. Adhesion Properties of Urea-modified Phenol Formaldehyde Resin for Plywood[J]. bce, 2018, 52(5): 20-24.

参考文献

[1] 陶毓博,李鹏,陆仁书,等. 尿素改性酚醛树脂胶粘剂的研究[J]. 林产工业,2005,32(1):6-13.
[2] 赵伟刚. 合成参数对尿素改性酚醛(PUF)树脂结构与性能的影响[D]. 昆明:西南林学院硕士学位论文,2009.
[3] 蒋玉凤. 苯酚尿素甲醛共缩聚树脂的合成、表征及其应用研究[D]. 南京:南京工业大学硕士学位论文,2011.
[4] GINDL M,REITERER A,SINN G,et al. Effects of surface ageing on wettability, surface chemistry, and adhesion of wood[J]. Holz als Roh-und Werkstoff,2004,62(4):273-280.
[5] 韩书广,黄润州,周兆兵,等. 预压缩杨木的动态润湿性[J]. 南京林业大学学报:自然科学版,2009,33(6):11-14.
[6] HUANG X N,KOCAEFE D,KOCAEFE Y,et al. Changes in wettability of heat-treated wood due to artificial weathering[J]. Wood Science and Technology,2012,46(6):1215-1237.
[7] MALDAS D C,KAMDEM D R. Surface tension and wettability of CCA-treated red maple[J]. Wood and Fiber Science,1998,30(4):368-373.
[8] NUSSBAUM R M. Natural surface inactivation of Scots pine and Norway spruce evaluated by contact angle measurements[J]. Holz als Roh-und Werkstoff,1999,57(6):419-424.
[9] WOLKENHAUER A,AVRAMIDIS G,CAI Y,et al. Investigation of wood and timber surface modification by dielectric barrier discharge at atmospheric pressure[J]. Plasma Processes and Polymers,2007,4(S1):S470-S474.
[10] SHI S Q,GARDNER D J. Dynamic adhesive wettability of wood[J]. Wood and Fiber Science,2001,33(1):58-68.
[11] LIPTAKOVA E,KUDELA J. Analysis of the wood-wetting process[J]. Holzforschung,1994,48(2):139-144.
[12] 刘振海. 分析化学手册:第八分册[M]. 北京:化学工业出版社,1998.
[13] 李淑君,陶毓博,李坚,等. 用TG-DSC-FTIR联用技术研究酚醛树脂的热解行为[J]. 东北林业大学学报,2007,35(6):56-58.
[14] 陈鸯飞,陈智琴,肖绍懿,等. 酚醛树脂热降解过程中的结构变化[J]. 热固性树脂,2008,23(4):4-8,12.
[15] 杨帆. 酚醛树脂与木材的相互作用[J]. 人造板通讯,1996(8):2-3.

胶合板用尿素改性酚醛树脂胶合性能的研究

Adhesion Properties of Urea-modified Phenol Formaldehyde Resin for Plywood

PDF (PC)

可视化

摘要/Abstract