欢迎访问《生物质化学工程》,

生物质化学工程 ›› 2020, Vol. 54 ›› Issue (5): 25-32.doi: 10.3969/j.issn.1673-5854.2020.05.004

• 研究报告 • 上一篇    下一篇

竹材液化墙体泡沫材料的阻燃改性

王盟盟1,2(),刘乐群1,2,3,*(),刘震涛1,3,赵莹1   

  1. 1. 浙江省林业科学研究院, 浙江 杭州 310023
    2. 浙江农林大学 工程学院, 浙江 杭州 311300
    3. 浙江工业大学 化学工程学院, 浙江 杭州 310004
  • 收稿日期:2020-03-13 出版日期:2020-09-30 发布日期:2020-09-29
  • 通讯作者: 刘乐群 E-mail:842752387@qq.com;llq234@sina.com
  • 作者简介:王盟盟(1994-),女,安徽阜阳人,硕士生,研究方向为生物质泡沫工程材料; E-mail:842752387@qq.com
  • 基金资助:
    浙江省省属科研院所专项(2017F30014);浙江省省级标准研究项目(SJ-BZ/2019090)

Flame Retardant Modification of Bamboo Liquefied Wall Foam Materials

Mengmeng WANG1,2(),Lequn LIU1,2,3,*(),Zhentao LIU1,3,Ying ZHAO1   

  1. 1. Zhejiang Academy of Forestry, Hangzhou 310023, China
    2. School of Engineering, Zhejiang A&F University, Hangzhou 311300, China
    3. School of Chemical Engineering, Zhejiang University of Technology, Hangzhou 310004, China
  • Received:2020-03-13 Online:2020-09-30 Published:2020-09-29
  • Contact: Lequn LIU E-mail:842752387@qq.com;llq234@sina.com
  • Supported by:
    浙江省省属科研院所专项(2017F30014);浙江省省级标准研究项目(SJ-BZ/2019090)

摘要:

为提高竹材液化产物所制备的高轻发泡墙体材料的防火性能,分别采用材料内部添加和表面浸泡的方法进行阻燃改性,并评价不同阻燃剂及其添加量对发泡材料阻燃性能的影响。实验结果表明:在材料内部或表面添加选择的阻燃剂不会对材料自身形貌或组分产生明显影响,对材料的力学性能亦不会造成破坏,在材料内部添加3 g膨胀型凝胶-二氧化硅/聚磷酸铵核壳阻燃剂(MCAPP)后压缩强度达到了0.37 MPa,在材料表面浸泡聚硅氧烷后压缩强度达到了0.58 MPa,同时能提高材料的阻燃性能,在材料内部添加聚磷酸铵(M-APP)后极限氧指数提高到33.2%,比改性前提高3%。在材料表面浸泡膨胀型壳聚糖-蒙脱土-聚磷酸铵(CMAp)后点燃时间明显延长,极限氧指数最高达到了31.5%。

关键词: 竹材, 发泡材料, 墙体材料, 阻燃改性

Abstract:

In order to improve the fireproof performance of the high-light foam wall materials prepared by the bamboo material liquefaction products, various methods of internal addition and surface immersion were used to carry out a variety of flame retardant modifications, and the effects of different flame retardants and their additions on the foam materials were evaluated. The expenmental effect of flame retardancy. The experimental results show that: adding the selected flame retardant inside or on the surface of the material will not have a significant impact on the morphology or composition of the material itself, and will not cause damage to the mechanical properties of the material. After adding 3 g of expanded gel-silica/ammonium polyphosphate core-shell flame retardant(MCAPP) inside the material, the compressive strength reached 0.37 MPa. The compressive strength after immersing the surface of the material with oxane reaches 0.58 MPa. At the same time, it can improve the flame retardance of the material. The limiting oxygen index increased to 33.2% after adding ammonium polyphosphate(M-APP) inside the material, which was 3% higher than before modification. After immersing the expanded chitosan-montmorillonite-ammonium polyphosphate(CMAp). The flame retardant was soaked on the surface of the material, the ignition time was significantly prolonged, and the limiting oxygen index reached 31.5%.

Key words: bamboo, foaming material, wall material, flame retardant modification

中图分类号: