双组分豆粕基胶黏剂的流变行为研究

王利军1, 夏成龙1, 许玉芝1,2, 南静娅1,2, 王春鹏1,2, 储富祥1,2   

  1. 1. 中国林业科学研究院 林产化学工业研究所;生物质化学利用国家工程实验室;国家林业局 林产化学工程 重点开放性实验室;江苏省 生物质能源与材料重点实验室, 江苏 南京 210042;
    2. 中国林业科学研究院 林业新技术研究所, 北京 100091
  • 收稿日期:2016-03-15 出版日期:2016-11-30 发布日期:2016-12-03
  • 通讯作者: 储富祥(1963-),男,研究员,博士生导师,主要从事林产化学研究;E-mail:chufuxiang@caf.ac.cn E-mail:chufuxiang@caf.ac.cn
  • 作者简介:王利军(1989-),男,河南郑州人,硕士生,主要从事豆粕胶黏剂的研究
  • 基金资助:
    浙江省与中国林科院省院合作项目(2014SY10);中国林科院林业新技术所基本科研业务费专项资金(CAFINT2015C03)

Rheological Properties of Two-component Soybean Based Adhesives

WANG Li-jun1, XIA Cheng-long1, XU Yu-zhi1,2, NAN Jing-ya1,2, WANG Chun-peng1,2, CHU Fu-xiang1,2   

  1. 1. Institute of Chemical Industry of Forest Products, CAF;National Engineering Lab. for Biomass Chemical Utilization;Key and Lab. of Forest Chemical Engineering, SFA;Key Lab. of Biomass Energy and Material, Jiangsu Province, Nanjing 210042, China;
    2. Research Institute of Forestry New Technology, CAF, Beijing 100091, China
  • Received:2016-03-15 Online:2016-11-30 Published:2016-12-03

摘要: 以改性胶液作为组分1,豆粕粉作为组分2,通过常温复配的技术手段制备了一种双组分豆粕基胶黏剂,并利用旋转流变仪对其流变行为进行了研究。结果表明:添加改性胶液的双组分豆粕基胶黏剂黏度增加,但剪切变稀现象与添加自来水的豆粕基胶黏剂保持一致;豆粕粉添加量对胶黏剂在高剪切速率下的流变行为的影响较为明显;Z试剂对胶黏剂在低配比(豆粕粉添加量≤10%)、低剪切速率(≤500 s-1)下的流变行为影响较大;填料和表面活性剂只影响豆粕基胶黏剂的黏度而不改变其剪切流变行为。

关键词: 双组分, 豆粕基胶黏剂, 流变行为

Abstract: Using modified glue as component 1 and soybean powder as component 2,the two-component soybean based adhesives were prepared by the compound technology at room temperature.The rotational rheometer was used to study the rheological behavior.The results showed that the viscosity of the soybean based adhesives increased by adding the modified glue,but the phenomenon of shear thinning was similar.The effect of the addition amount of soybean powder on the rheological behavior was more obvious at higher shear rate.The rheological behavior was affected greatly by Z reagent in lower ratio (soybean powder dosage ≤10%)and shear rate (≤500 s-1).Filling and surfactants took only impact on the viscosity of soybean based adhesives,but they did not change the rheological behaviors.

Key words: two-component, soybean based adhesives, rheological properties